Print Email Facebook Twitter Repairing impacted thermoplastic composites using ultrasonic welding to restore the compressive strength Title Repairing impacted thermoplastic composites using ultrasonic welding to restore the compressive strength Author Vreeken, Joost (TU Delft Aerospace Engineering) Contributor Pascoe, J.A. (mentor) Villegas, I.F. (graduation committee) Degree granting institution Delft University of Technology Programme Aerospace Engineering Date 2022-06-22 Abstract This research project investigates the potential use of ultrasonic welding as a tool to repair impact damage inside thermoplastic composites to restore the compressive strength. Compared to the already existing method, hot-pressing, ultrasonic welding could offer faster processing times, no need for dedicated tooling, smaller and lighter machinery and a smaller (heat) affected zone. It was shown that ultrasonic welding is able to melt and re-consolidate delaminations, decreasing the damaged area. However, even when using the same welding parameters, the process showed large variations between the welds. These variations should be minimized for the process to be usable as a repair process.Compression after impact (CAI) testing showed that welded repairs are able to fully restore the CAI strength. The re-consolidated material inside the damaged area suppresses local buckling, which normally causes premature failure. However, it was also shown that repairs with little re-consolidated material can decrease the CAI strength. Subject Impact damageRepairThermoplasticsUltrasonic weldingCompressive strengthCompositesCompression after impact To reference this document use: http://resolver.tudelft.nl/uuid:78ed96f0-1a52-49ac-b180-4ea8e34e8b35 Part of collection Student theses Document type master thesis Rights © 2022 Joost Vreeken Files PDF Thesis_Joost_Vreeken_4268 ... 6_2022.pdf 100.89 MB Close viewer /islandora/object/uuid:78ed96f0-1a52-49ac-b180-4ea8e34e8b35/datastream/OBJ/view